Stainless Steel 422 Bolts are made up of chromium based martensitic stainless steel that has 11.5% chromium, nickel, molybdenum and tungsten for stabilization. Suraj Metal Corporationis a leading manufacturer and supplier of the SS 422 Hex Bolt and other different types of fasteners. The material also has sulfur, phosphorus, silicon, manganese and iron in the composition.
The ASTM A565 AISI 422 Nut Bolt can be used in different applications such as oil and gas, transportation, storage tanks, panels, rails and other different applications that have high wear and tear properties. The AMS 5655 Stud Bolts are one type of fasteners that are used to drive into a narrow hole to fix other components on both sides. Similarly, the 422 Stainless Steel Dowel Pins are also used in specific circumstance to connect two components together. There are also threaded rods that can have threads on one end or on both ends. The 422 Stainless Steel Threaded Rod can be used in high stress applications such as machine parts and mechanical components. There are other types of fasteners that do not need nuts to fasten. The UNS S42200 SS 422 Screw is driven into the bolt hole with screw drivers. There are different types of screws depending on the shapes, slots and thread type. We supply all types of fasteners such as the 1.4935 SS 422 Bolts and Nuts and others in different dimensions, specifications and standards. Please feel free to contact us for more information and pricing on more different types such as the SS 422 Washer.
| Material | Specification | Standards | Length | Size |
| 410 Stainless Steel Fasteners | IS BS ASTM |
DIN, ISO, JIS, GB, IS, BS, ASTM | 3 mm to 200 mm | M 02 to M 160 |
| Component | Wt. % |
| C | 0.23 |
| Cr | 12.5 |
| Fe | 83 |
| Mn | 0.5 |
| Mo | 1 |
| Ni | 0.8 |
| P | 0.02 |
| S | 0.015 |
| Si | 0.38 |
| V | 0.23 |
| W | 1 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 290 | 290 | Estimated from Rockwell C value for Brinell test with 3000 kg load/10 mm diameter ball |
| Hardness, Knoop | 315 | 315 | Estimated from Rockwell C value. |
| Hardness, Rockwell C | 30 | 30 | |
| Hardness, Vickers | 304 | 304 | Estimated from Rockwell C value. |
| Tensile Strength, Ultimate | 897 MPa | 130000 psi | |
| Tensile Strength, Yield | 828 MPa | 120000 psi | 0.2% Offset |
| Elongation at Break | 15 % | 15 % | |
| Reduction of Area | 40 % | 40 % |